Forsterite was synthesized with MgCO3 and SiO2 powders using a solid-state method at 1200–1300°C. The ceramic specimen with the highest forsterite phase content was sintered with the ZrO2 sintering aid at mass fractions of 0.5, 1.0, and 1.5 wt% at 1400°C for 4 h. The dielectric constant and loss tangent were also measured via the waveguide method at 8–12 GHz. The formation of enstatite and cristobalite was minimized through precise synthesis temperature control. Phase measurement by the Rietveld method showed that specimen F28 contained more than 99.8% forsterite. It was found that ZrO2 reduced the pore volume percent and increased the density even at low mass fractions. A liquid phase on the grain boundaries was demonstrated. The solid ceramic specimen F28-15Z showed a dielectric constant of 6.5 and high quality factor of 189000.